Color is gray-white in a plated condition. Had very high luster in fused conditions. Soft, but is very ductile. Corrosion resistance is good. (Coated items should meet 24 hour 5% salt spray requirements.) Solderability is excellent.
Tin is not good for low temperature applications 9changes structure and loses adhesion when exposed to temperature below 40 C). If a bright finish is desired to be used in lieu of fused tin, specify Bright Tin plate. Thickness can exceed that of fused tin and deposit shows excellent corrosion resistance and solderability.
Type I: Standard specification.
Type II: Hot dipped.
As specified on drawing. Thickness guide not part of Spec.
.0001" - .00025" Flash for soldering.
.0002" - .0004" To prevent galling and seizing.
.0003" min Where corrosion resistance is important.
.0002" - .0006" To prevent formation of case during nitriding.
Color is gray-white in a plated condition. Had very high luster in fused conditions. Soft, but is very ductile. Corrosion resistance is good. (Coated items should meet 24 hour 5% salt spray requirements.) Solderability is excellent. 
Tin is not good for low temperature applications 9changes structure and loses adhesion when exposed to temperature below 40 C). If a bright finish is desired to be used in lieu of fused tin, specify Bright Tin plate. Thickness can exceed that of fused tin and deposit shows excellent corrosion resistance and solderability.